Cold spray equipment is successfully used to apply a variety of materials on a very broad range of metallic, ceramic, and plastic substrates.   VRC Metal Systems Cold Spray equipment is used for depositing the materials below:


Copper Alloys, applied by cold spray equipment

CP Cu, Commercially Pure Copper on 1100 Copper substrate, Adhesion Strength over 10,000 psi  [68 MPa], Hardness: 180 HV


DT 31, Adhesion > 10,000 psi [68 MPa], Tensile strength > 56,000 [386 MPa]

500A Cu, 500A Copper on Aluminium 7075,  Adhesion Strength > 10,000 [68 MPa],  Hardness: 190 HV

Other Metals applied by cold spray equipment

CP Ni, Commerically Pure Nickel on Aluminum, Adhesion Strength > 10,000 [68 MPa] 3-lug Shear Strength > 18 ksi [124 MPa] , Hardness: 210 HV

CP Ti,  Commercially Pure Titanium on Ti 6Al-4V,  Adhesion Strength > 10 ksi [68 MPa]

Tantalum,  40 ksi [275 MPa] while maintaining > 3% ductility are repeatable., Tantalum is dark (blue-gray),[21] dense, ductile, very hard, easily fabricated, and highly conductive of heat and electricity. The metal is renowned for its resistance to corrosion by acids; in fact, at temperatures below 150 °C tantalum is almost completely immune to attack by the normally aggressive aqua regia. 

316 SS and Chrome Carbide, Adhesion strength > 10 ksi [68 MPa], High strengths > 100 ksi [689 MPa] 

Ti + BAM,  BAM is a unique and patented high hardness low-friction material developed by AMES and can be licensed from New Tech Ceramics.