COLD SPRAY MATERIALS/ Cold Spray Powders
Cold spray equipment is successfully used to apply a variety of materials on a very broad range of metallic, ceramic, and plastic substrates. VRC Metal Systems Cold Spray equipment is used for depositing the materials below:
Copper Alloys, applied by cold spray equipment
CP Cu, Commercially Pure Copper on 1100 Copper substrate, Adhesion Strength over 10,000 psi [68 MPa], Hardness: 180 HV
DT 31, Adhesion > 10,000 psi [68 MPa], Tensile strength > 56,000 [386 MPa]
500A Cu, 500A Copper on Aluminium 7075, Adhesion Strength > 10,000 [68 MPa], Hardness: 190 HV
Other Metals applied by cold spray equipment
CP Ni, Commerically Pure Nickel on Aluminum, Adhesion Strength > 10,000 [68 MPa] 3-lug Shear Strength > 18 ksi [124 MPa] , Hardness: 210 HV
CP Ti, Commercially Pure Titanium on Ti 6Al-4V, Adhesion Strength > 10 ksi [68 MPa]
Tantalum, 40 ksi [275 MPa] while maintaining > 3% ductility are repeatable., Tantalum is dark (blue-gray), dense, ductile, very hard, easily fabricated, and highly conductive of heat and electricity. The metal is renowned for its resistance to corrosion by acids; in fact, at temperatures below 150 °C tantalum is almost completely immune to attack by the normally aggressive aqua regia.
316 SS and Chrome Carbide, Adhesion strength > 10 ksi [68 MPa], High strengths > 100 ksi [689 MPa]
Ti + BAM, BAM is a unique and patented high hardness low-friction material developed by AMES and can be licensed from New Tech Ceramics.
Learn more about cold spray equipment, and cold spray processes by connecting with us